Ceramic
Coating and Metal Repair Kit for Corrosion
Control |
|
AM-A
and CERACOT
Ceramic-Metallic
Rebuilding Grades
For repair and strenthening and reconditioning
of welded part of steels and damaged
area, worn-out steel surface of ships,
equipment, machinery, structures, pipes,
tanks, and ect., |
AM-C
ITEMS
Ceramic-Metallic
Corrosion Resistance Coating Grades
For coating applications on a wide range
of industrial materials to protect from
corrosion and erosion attacks, especially
on marine facilities. Specific Grades
effective to different coating work
conditions and environmental classifications
are available. |
Mix
proportion (at ambient temperature 20°C)
:
Base to Hardener: 5 to 1 by weight,
3 to 1 by volume
|
| Grade |
Volume
Solids |
Pot
Life |
Over
Coating Interval |
Shelf
Life |
| AM-A |
93% |
20-30
Min |
24
Hours |
1
Year |
| AM-C |
87% |
40-60
Min |
24
Hours |
1
Year |
|
|
 |
Product
Packings:
per set of Base and Hardener
AM-A: 1kg in plastic kit
AM-C: 1kg in plastic kit
and 20 kg in
steel
can
CERACOT: 60g, 100g in tube
PRIMER PAINT: 22kg in steel
can |
|
|
|
|
| PROPERTIES |
| Description
\ Item |
AM-A
Ceramic Metal Rebuilding |
AM-C
Ceramic Metal Coating |
| Specific
Gravity |
2.0
~ 2.2 |
1.6
~ 1.8 |
| Rockwell
hardness, R scale |
100
~ 114 |
100
~ 112 |
| Adhesive
strength, MPa |
16
~ 22 |
15
~ 20 |
| Resistance
to heat |
250
~ 280 ° C |
200
~ 230 ° C |
| Resistance
to Chemicals |
No
effect after 168hrs in 5% H2SO4 or NaOH |
| Resistance
to oil |
No
effect after 168hrs |
| Resistance
to gasoline |
No
effect after 168hrs |
| Resistance
to ozone |
No
effect after 48hrs in ozone 10ppm, 40
° C |
| Resistance
to thermal change |
No
cracks in 2cycles of -20 ° C and
80 ° C |
| Resistance
to pressure, 6.8MPa |
No
failure in applied section |
| Resistance
to impact |
No
defects by 73.5kN hammering |
| Resistance
to salt spray |
No
effect in 3.5% NaCI, 4000hrs accelerated
test |
| Flexibility |
No
cracks mandrel bend test, Ø10mm
bar |
| Toxicity |
Not
toxic when cured |
Benefits
-
Does not break down or change under
severe environmental surroundings.
-
Is not flammable or explosive nor is
a pollutant.
-
Maintains strong adhesive strength and
acts as a cold welding agent.
-
Is machinable after rebuilding damage
part.
-
Is evnironmentally friendly due to low
volatile organic compound level.
-
Is applicable on damp and wet surfaces
-
Is simple applied benefited by basically
single coat system.
- Is
long-term cost saving system due to
longer durability.
|
|
|
|